POM1100G15
POM Materials
Glass fiber 15% reinforced,
high strength, high modulus.
| Testing Item | ASTM | Unit | Value | ||||
|---|---|---|---|---|---|---|---|
|
Tensile strength Tensile elongation |
D-638 D-638 |
Kg/cm2 % |
1100 4.0 |
||||
|
Flexural strength Flexural modulus |
D-790 |
Kg/cm2 Kg/cm2 |
1800 42000 |
||||
|
Izod impact (1/8", V-notched) |
D-256 |
Kg‧cm/cm ( 23°C ) ( -30°C ) |
9.0 - |
||||
|
Heat distortion temperature |
D-648 |
°C (18.6Kg/cm2) |
145 | ||||
| Melt index | D-1238 |
g/10min (190°C/2.16kg) (275°C/2.16kg) |
5.0 - |
||||
| Hardness | D-785 | Rockwell M | 82 | ||||
| Mold shrinkage | D-955 |
|
0.5 0.9 |
||||
| Specific gravity | D-792 | - | 1.50 | ||||
| Ash content | D-482 | % | 15(GF) | ||||
| Flammability | UL-94 | 1/16" | HB |
POM, Glass fiber 15% reinforced, high strength, high modulus.
Pretreatment：23℃,50%RH,24hrs