NB7200G33
PA66 Materials
Glass fiber 33% reinforced,
high flow, black colored.
| Testing Item | ASTM | Unit | Value | ||||
|---|---|---|---|---|---|---|---|
|
Tensile strength Tensile elongation |
D-638 D-638 |
Kg/cm2 % |
1750 3.0 |
||||
|
Flexural strength Flexural modulus |
D-790 |
Kg/cm2 Kg/cm2 |
2700 90000 |
||||
|
Izod impact (1/8", V-notched) |
D-256 |
Kg‧cm/cm ( 23°C ) ( -30°C ) |
10.0 - |
||||
|
Heat distortion temperature |
D-648 |
°C (18.6Kg/cm2) |
250 | ||||
| Melting point | DSC | °C | 250~260 | ||||
| Hardness | D-785 | Rockwell R | 121 | ||||
| Mold shrinkage | D-955 |
|
0.3 0.8 |
||||
| Specific gravity | D-792 | - | 1.40 | ||||
| Ash content | D-482 | % | 33(GF) | ||||
| Flammability | UL-94 | 1/16" | HB |
NYLON 66, Glass fiber 33% reinforced, high flow, black colored.
Pretreatment：23℃,50%RH,24hrs