NA1200GH50
PA6 Materials
Glass fiber 50% reinforced,
low warpage、high modulus、 high impact.
| Testing Item | ASTM | Unit | Value | ||||
|---|---|---|---|---|---|---|---|
|
Tensile strength Tensile elongation |
D-638 D-638 |
Kg/cm2 % |
2250 3.0 |
||||
|
Flexural strength Flexural modulus |
D-790 |
Kg/cm2 Kg/cm2 |
3800 130000 |
||||
|
Izod impact (1/8", V-notched) |
D-256 |
Kg‧cm/cm ( 23°C ) ( -30°C ) |
20.0 - |
||||
|
Heat distortion temperature |
D-648 |
°C (18.6Kg/cm2) |
220 | ||||
| Melting point | DSC | °C | 215~225 | ||||
| Hardness | D-785 | Rockwell R | 121 | ||||
| Mold shrinkage | D-955 |
|
0.1 0.3 |
||||
| Specific gravity | D-792 | - | 1.55 | ||||
| Ash content | D-482 | % | 50(GF) | ||||
| Flammability | UL-94 | 1/16" | HB |
NYLON 6,Glass fiber 50% reinforced,low warpage、
high modulus、high impact.
high modulus、high impact.
Pretreatment：23℃,50%RH,24hrs